(FAQ)Answers to questions in the production of six-high reversing mills, cold rolling technology

Table of Contents

[vc_row][vc_column][vc_toggle title=”What are the reasons for the strip broken?”]

  1. Incoming materials The incoming materials have serious quality defects, such as waste edge pressing, overflow edge, under-pickling, over-pickling, uneven thickness, plate-shaped edge waves and middle waves, etc., which may cause belt breakage.
  2. Equipment failure Electrical, control system failure or hydraulic system failure. The common ones are tension fluctuation, tension disappearance, hydraulic system, emulsion system shutdown, etc.
  3. Operation failure The belt breakage caused by the operation accident is more common. The deviation of the strip and the defects of incoming materials were not detected and taken measures in time; the selection of the pass plan was unreasonable, the deformation of the pass was too large, the rolling pressure was large, and the shape of the plate was difficult to control; the tension before and after the pass was too large and the strip was broken. ; The thickness fluctuates somewhere in the previous pass, and the current pass has not been adjusted and decelerated in time.
  4. Belt breakage caused by roll burst

[/vc_toggle][vc_toggle title=”How to deal with the broken belt?”]After the belt is broken, stop immediately, pull out the strip steel in the frame and pull out the middle roll (backup roll) of the work roll to check whether the roll is stuck and damaged, and the roll should be replaced if damaged. And clean up the broken belt debris in the archway. Check the main drive shaft of the rolling mill and the safety pin for breakage, and replace it in time if the breakage is found. The rolling speed of the first coil after changing the rolls should not be too fast, and the surface quality of the strip should be carefully checked.[/vc_toggle][vc_toggle title=”How are thermal scratches caused?”]Because the flow rate of the emulsion during high-speed rolling is too small, the thermal deformation generated cannot be taken away in time, so that the temperature of the roll rises, the emulsion oil film on the surface of the strip is broken, and the surface of the strip is scratched. In addition, the roll slips at high speed, and the strip and the roll produce relative friction, which will also cause thermal scratches. Thermal scratches have a lighter scratch depth on the surface of the strip, and basically have no feel.[/vc_toggle][vc_toggle title=”How to control thermal scratch?”]

  1. Increase the flow rate of the emulsion.
  2. Lower the temperature of the emulsion.
  3. There are many reasons for roll slippage at high speed, whether the input of roll diameter is correct. Whether the current difference between the upper and lower work rolls is too large. Whether the roughness of the intermediate roll backup roll is consistent. Whether the pressing force is too small, etc.

[/vc_toggle][vc_toggle title=”How are hard scratches caused?”]The working time of the work roll is too long, the surface roughness of the roll is reduced, and the deformation of the pass is too large. Make the roll slip on the surface of the strip, which is easy to cause hard scratches. Generally, hard scratches appear when the deformation of the strip is large. For example, 1 or 2 passes. Hard scratches have more obvious scratches and deeper scratches.[/vc_toggle][vc_toggle title=”How to control the 1st and 2nd pass hard scratches?”]When the roughness of the roll is low, the roll is not replaced in time. The first and second pass hard scratches are controlled as follows. 1. First of all, increase the tension of the strip outlet and reduce the tension of the strip inlet. 2. When starting the rolling mill, the pressing thickness should not be too thin, but should be pressed slowly to the set thickness. 3. Do not directly reduce the speed when reducing the speed, so as to avoid thickness fluctuations. Excessive deformation in places with thin thickness fluctuations may cause scratches. 4. If there are slippery stripes on the surface of the strip during rolling, change the thickness of the outlet in time to reduce the amount of deformation. Change the roll after this pass.[/vc_toggle][/vc_column][/vc_row][vc_row][vc_column][vc_btn title=”About LMM GROUP” link=”url:https%3A%2F%2Fwww.lmmgroupcn.com%2Fabout-lmm%2F|target:_blank”][vc_column_text css=”.vc_custom_1649296177864{margin-top: 50px !important;}”]friendship Link:

LMM Totai Refractory, LMM Mill ROLLS, LMM CCM, LMM Mechanical Equipment, Intelligent industry, STEEL Metallurgy Industry[/vc_column_text][/vc_column][/vc_row]

Facebook
Twitter
LinkedIn
Reddit

As professional one-stop solution provider, LIAONING MINERAL & METALLURGY GROUP CO., LTD(LMM GROUP) Established in 2007, and focus on engineering research & design, production & delivery, technology transfer, installation & commissioning, construction & building, operation & management for iron, steel & metallurgical industries globally. 

Our product  have been supplied to world’s top steel manufacturer Arcelormittal, TATA Steel, EZZ steel etc. We do OEM for Concast and Danieli for a long time.

LMM Main product series

Core technology products:

  • magnesia carbon brick
  • slide gate plate
  • graphite electrode

Core technology products:

  • Hss roller
  • cast steel rolls
  • tungten carbide ring roller

Core technology products:

  • copper mould tube
  • copper mould plate
  • assembly & cooling jackts

Need For Some Help ?

Professional engineers provide solutions and technical drawings

phone

86(411) 84174804

mail

lmme-business@lmmgroup.com.cn

Special product design, please send specific data and drawings to our mailbox or form.

As professional one-stop solution provider, LIAONING MINERAL & METALLURGY GROUP CO., LTD(LMM GROUP) Established in 2007, and focus on engineering research & design, production & delivery, technology transfer, installation & commissioning, construction & building, operation & management for iron, steel & metallurgical industries globally. 

Our product  have been supplied to world’s top steel manufacturer Arcelormittal, TATA Steel, EZZ steel etc. We do OEM for Concast and Danieli for a long time.

LMM GROUP Certification

LMM GROUP Service

Get A Free Consultation
And Estimate